2-(7-methyloctyl)phenol

Conditions: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 0.2 part by weight of the sodium salt of a sulfated addition product of triisobutylphenol and 7 mols of ethylene oxide (emulsifier A) and 0.02 part by weight of potassium peroxodisulfate are dissolved in 61.5 parts by weight of completely desalted water at 80° C. in a polymerization vessel provided with a reflux condenser, stirrer, thermometer, and feed vessel. An emulsion, earlier prepared from 83 parts by weight of ethyl acrylate, 10 parts by weight of methoxy polyethyleneglycol methacrylate [formula (I), n=15], 5 parts by weight of disodium itaconate, 1.2 parts by weight of N-hydroxymethyl methacrylamide, 0.8 part by weight of methacrylamide, 2.3 parts by weight of emulsifier A, 1 part by weight of the addition product formed between isononylphenol and 100 mols of ethylene oxide (emulsifier B), 0.18 part by weight of potassium peroxodisulfate, and 94 parts by weight of desalted water, is added dropwise to this solution at 80° C. over a period of 4 hours. After addition is complete, the reaction temperature is kept for one further hour at 80° C. and subsequently the mixture is cooled to room temperature. A coagulate-free dispersion having a solids content of about 40% is obtained. provided with a reflux condenser, stirrer

Conditions: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 0.2 part by weight of the sodium salt of a sulfated addition product of triisobutylphenol and 7 mols of ethylene oxide (emulsifier A) and 0.02 part by weight of potassium peroxodisulfate are dissolved in 61.5 parts by weight of completely desalted water at 80° C. in a polymerization vessel provided with a reflux condenser, stirrer, thermometer, and feed vessel. An emulsion, earlier prepared from 83 parts by weight of ethyl acrylate, 10 parts by weight of methoxy polyethyleneglycol methacrylate [formula (I), n=15], 5 parts by weight of disodium itaconate, 1.2 parts by weight of N-hydroxymethyl methacrylamide, 0.8 part by weight of methacrylamide, 2.3 parts by weight of emulsifier A, 1 part by weight of the addition product formed between isononylphenol and 100 mols of ethylene oxide (emulsifier B), 0.18 part by weight of potassium peroxodisulfate, and 94 parts by weight of desalted water, is added dropwise to this solution at 80° C. over a period of 4 hours. After addition is complete, the reaction temperature is kept for one further hour at 80° C. and subsequently the mixture is cooled to room temperature. A coagulate-free dispersion having a solids content of about 40% is obtained. provided with a reflux condenser, stirrer

Conditions: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 0.2 part by weight of the sodium salt of a sulfated addition product of triisobutylphenol and 7 mols of ethylene oxide (emulsifier A) and 0.02 part by weight of potassium peroxodisulfate are dissolved in 61.5 parts by weight of completely desalted water at 80° C. in a polymerization vessel provided with a reflux condenser, stirrer, thermometer, and feed vessel. An emulsion, earlier prepared from 83 parts by weight of ethyl acrylate, 10 parts by weight of methoxy polyethyleneglycol methacrylate [formula (I), n=15], 5 parts by weight of disodium itaconate, 1.2 parts by weight of N-hydroxymethyl methacrylamide, 0.8 part by weight of methacrylamide 2.3 parts by weight of emulsifier A, 1 part by weight of the addition product formed between isononylphenol and 100 mols of ethylene oxide (emulsifier B), 0.18 part by weight of potassium peroxodisulfate, and 94 parts by weight of desalted water, is added dropwise to this solution at 80° C. over a period of 4 hours. After addition is complete, the reaction temperature is kept for one further hour at 80° C. and subsequently the mixture is cooled to room temperature. A coagulate-free dispersion having a solids content of about 40% is obtained. provided with a reflux condenser, stirrer

Conditions: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: An aqueous emulsion comprising 45 parts by weight of methylmethacrylate, 7 parts by weight of styrene, 48 parts by weight of n-butylacrylate, and containing 0.18 part by weight of 30 percent hydrogen peroxide and 0.95 part by weight of C14 -fatty amine hydrochloride dissolved therein, is added dropwise at 85°C. over a period of 4 - 6 hours to an aqueous solution comprising 0.05 part by weight of C14 -fatty amine hydrochloride, 0.005 part by weight of iron (II) chloride, and 0.02 part by weight of 30 percent hydrogen peroxide. The dispersion obtained is subsequently combined with 4 parts by weight of an adduct formed between isononyl phenol and 100 mols of ethylene oxide. A coagulate-free dispersion having a solids content of about 50 percent is obtained. dissolved is added dropwise at 85°C. over a period of 4 - 6 hours to an aqueous solution The dispersion obtained