tert-butyl octaneperoxoate

Conditions: temp:0.00; pressure:0.00; stir:

Conditions: temp:130.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 10.76 g of N-vinyl-2-pyrrolidone and the temperature is raised to 130° C. Then 0.9 g of tert-butyl perbenzoate is added. After 1 and 2 hours, respectively, a 0.4 g portion of tert-butyl perbenzoate is fed in. The charge is maintained at 130° C. for another 5 hours. A clouded viscous solution is obtained. After 1 and 2 hours A clouded viscous solution is obtained

Conditions: temp:130.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 10.76 g of N-vinyl-2-pyrrolidone and the temperature is raised to 130° C. Then 0.9 g of tert-butyl perbenzoate is added. After 1 and 2 hours, respectively, a 0.4 g portion of tert-butyl perbenzoate is fed in. The charge is maintained at 130° C. for another 5 hours. A clouded viscous solution is obtained. After 1 and 2 hours A clouded viscous solution is obtained

Conditions: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 2 h after the end of the addition, 1 g of tert-butyl peroctoate is fed in. The total polymerization time is 8 h. After the end of polymerization, the mixture is diluted with 590.0 g of dibutyl phthalate. An almost clear, viscous solution is obtained. After the end of polymerization An almost clear, viscous solution is obtained

Conditions: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 2 h after the end of the addition, 1 g of tert-butyl peroctoate is fed in. The total polymerization time is 8 h. After the end of polymerization, the mixture is diluted with 590.0 g of dibutyl phthalate. An almost clear, viscous solution is obtained. After the end of polymerization An almost clear, viscous solution is obtained

Conditions: temp:0.00; pressure:0.00; stir:

Conditions: temp:130.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 10.76 g of N-vinyl-2-pyrrolidone and the temperature is raised to 130° C. Then 0.9 g of tert-butyl perbenzoate is added. After 1 and 2 hours, respectively, a 0.4 g portion of tert-butyl perbenzoate is fed in. The charge is maintained at 130° C. for another 5 hours. A clouded viscous solution is obtained. After 1 and 2 hours A clouded viscous solution is obtained

Conditions: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

Procedure: 2 h after the end of the addition, 1 g of tert-butyl peroctoate is fed in. The total polymerization time is 8 h. After the end of polymerization, the mixture is diluted with 590.0 g of dibutyl phthalate. An almost clear, viscous solution is obtained. After the end of polymerization An almost clear, viscous solution is obtained